Effect of mouthwashes on the microhardness of aesthetic composite restorative materials
DOI:
https://doi.org/10.23938/ASSN.1049Keywords:
Resin composite, Vickers’ Hardness, Mouthwashes, Microhardness, pHAbstract
Background. Mouthwashes are increasingly being used worldwide. However, these preparations are known to have a negative impact on composite resin dental restorations. In this study, we aim to evaluate the effect of mouthwashes on the microhardness of such restorations.
Methods. Thirty specimens of Tetric N-Ceram composite were prepared. Each composite specimen was cured for 40 seconds and kept in saline solution for 24 hours at 37 °C. Baseline microhardness of each specimen was recorded using an Innovatest Vickers Micro Hardness Tester. Composite specimens were randomly placed in 20 mL of the selected mouthwashes (Colgate® Plax, Listerine® Teeth & Gum Defence, and Closeup® Antibacterial Mouthwash Cool Breeze) and stored in an incubator for 24 hours at 37 °C. Next, microhardness values were rechecked. pH measurements were recorded for each type of mouthwash using a digital pH meter.
Results. Due to the acidic nature of Colgate® and Listerine®, the microhardness of the restorations decreased with these mouthwashes; Listerine® caused the greatest decrease in microhardness and had the lowest pH reading (4.34). For Closeup®, with a neutral pH (7.02), no negative effect on microhardness was found; on the contrary, due to the presence of zinc in this latter mouthwash, an increase of the microhardness was found.
Conclusions. We confirm the negative effect of acidic mouthwashes on the microhardness of composite dental restorations.
Downloads
References
ALI Z, ELIYAS S, VERE JW. Choosing the right dental material and making sense of the options: evidence and clinical recommendations. Eur J Prosthodont Restor Dent 2015; 23(3): 150-162.
ALMEIDA GS, POSKUS LT, GUIMARÃES JG, DA SILVA EM. The effect of mouthrinses on salivary sorption, solubility and surface degradation of a nanofilled and a hybrid resin composite. Oper Dent 2010; 35(1): 105-111. http://doi.org/10.2341/09-080-l
DE PAULA AB, FUCIO SBP, AMBROSANO GMB, ALONSO RCB, SARDI JCO, PUPPIN-RONTANI RM. Biodegradation and abrasive wear of nano restorative materials. Oper Dent 2011; 36(6): 670-677. https://doi.org/10.2341/10-221-L
FESTUCCIA MS, GARCIA LD, CRUVINEL DR, PIRES-DE-SOUZA FD. Color stability, surface roughness and microhardness of composites submitted to mouthrinsing action. J Appl Oral Sci 2012; 20(2): 200-205. http://doi.org/10.1590/s1678-77572012000200013
VOLTARELLI FR, DOS SANTOS-DAROZ CB, ALVES MC, CAVALCANTI AN, MARCHI GM. Effect of chemical degradation followed by toothbrushing on the surface roughness of restorative composites. J Appl Oral Sci 2010; 18(6): 585-590. https://doi.org/10.1590%2FS1678-77572010000600009
SRIPETCHDANOND J, LEEVAILOJ C. Wear of human enamel opposing monolithic zirconia, glass ceramic, and composite resin: an in vitro study. J Prosthet Dent 2014; 112(5): 1141-1150. https://doi.org/10.1016/j.prosdent.2014.05.006
DOS SANTOS PA, GARCIA PPNS, DE OLIVEIRA ALBM, CHINELATTI MA, PALMA-DIBB RG. Chemical and morphological features of dental composite resin: influence of light curing units and immersion media. Microsc Res Tech 2010; 73(3): 176-181. https://doi.org/10.1002/jemt.20769
TOZ AKALIN T, GENC G, KORKMAZ CEYHAN Y, OZTURK BOZKURT F. The effect of mouth rinses on the color stability of sonicfill and a nanohybrid composite. J Istanb Univ Fac Dent 2016; 50(2): 17-23. https://doi.org/10.17096%2Fjiufd.15743
MIRANDA DDE A, BERTOLDO CE, AGUIAR FHB, LIMA DANL, LOVADINO JR. Effects of mouthwashes on Knoop hardness and surface roughness of dental composites after different immersion times. Braz Oral Res 2011; 25(2): 168-173. https://doi.org/10.1590/s1806-83242011000200012
ANTONY FERNANDEZ RA, EL ARABY M, SIBLINI M, AL-SHEHRI A. The effect of different types of oral mouth rinses on the hardness of Silorane-based and Nano-hybrid composites. Saudi J Oral Sci 2014; 1(2): 105-109. http://doi.org/10.4103/1658-6816.138481
SHIN S, KIM YJ, TOAN M, KIM JG, NGUYEN TP, CHO JK. Property enhancement of dental composite prepared with an isosorbide-based photocurable compound by mixing with TEGDMA. Eur Polym J 2017; 92: 338-345. https://doi.org/10.1016/j.eurpolymj.2017.05.009
ZHOU X, HUANG X, LI M, PENG X, WANG S, ZHOU X, CHENG L. Development and status of resin composite as dental restorative materials. J Appl Polym Sci 2019; 136(44): 48180-48192. https://doi.org/10.1002/app.48180
YADAV R, KUMAR M. Dental re1storative composite materials: A review. J Oral Biosci 2019; 61(2): 78-83. https://doi.org/10.1016/j.job.2019.04.001
BADRA VV, FARAONI JJ, RAMOS RP, PALMA-DIBB RG. Influence of different beverages on the microhardness and surface roughness of resin composites. Oper Dent 2005; 30(2): 213-219. Enlace
DE MORAES RR, MARIMON JLM, SCHNEIDER LF, SINHORETI MAC, CORRER-SOBRINHO L, BUENO M. Effects of 6 months of aging in water on hardness and surface roughness of two microhybrid dental composites. J Prosthodont 2008; 17(4): 323-326. https://doi.org/10.1111/j.1532-849x.2007.00295.x
GEORGE R, KAVYASHREE G. Effect of four mouth rinses on microhardness of esthetic restorative material: An in vitro study. J Int Oral Health 2017; 9(2): 55-59. http://doi.org/10.4103/jioh.jioh_21_16
KOCCHAR R, DEWAN R, SOI S, PUNJABI M. An evaluation and comparison of the effect of five mouthrinses on the microhardness of esthetic hybrid composite restorative material-an in vitro study. J Dent Spec 2017; 5(1): 66-69. https://www.jdsits.in/journal-article-file/4248
DALMIA S, AHER G, GULVE M, SAMUEL R, KOLHE S. Comparative evaluation of the effect of chlorhexidine based mouthwash and herbal mouthwash on the microhardness of two different composite resins an in vitro study. Int J Adv Res 2018; 6: 306-311. http://doi.org/10.21474/IJAR01/6679
ARMAS-VEGA A, CASANOVA-OBANDO P, TABOADA-ALVEAR MF, ALDAS-RAMÍREZ JE, MONTERO-OLEAS N, VITERI-GARCÍA A. Effect of mouthwashes on the integrity of composite resin and resin modified glass ionomer: In vitro study. J Clin Exp Dent 2019; 11(2): e179-e184. https://doi.org/10.4317/jced.55102
GÜRGAN S, ONEN A, KÖPRÜLÜ H. In vitro effects of alcohol-containing and alcohol-free mouthrinses on microhardness of some restorative materials. J Oral Rehabil 1997; 24(3): 244-246. https://doi.org/10.1111/j.1365-2842.1997.tb00321.x
URBANO CD, ABRAHÃO ALS, LANCELLOTTI AC, DE MENEZES-OLIVEIRA MAH, CALABREZ-FILHO, GONÇALVES L DE S. Effect of mouthrinses on surface roughness and of a nanofilled restorative composite. Braz Dent Sci 2014; 17(3): 92-97. http://doi.org/10.14295/bds.2014.v17i3.1014
COLOMBO M, GALLO S, POGGIO C, RICALDONE V, ARCIOLA CR, SCRIBANTE A. New Resin-Based Bulk-Fill Composites: in vitro Evaluation of Micro-Hardness and Depth of Cure as Infection Risk Indexes. Materials (Basel) 2020; 13(6): 1308-1321. https://doi.org/10.3390/ma13061308
HASHEMIKAMANGAR SS, POURHASHEMI SJ, TALEBI M, KIOMARSI N, KHARAZIFARD MJ. Effect of organic acids in dental biofilm on microhardness of a silorane-based composite. Restor Dent Endod 2015; 40(3): 188-194. https://doi.org/10.5395/rde.2015.40.3.188
KHOSRAVI M, ESMAEILI B, NIKZAD F, KHAFRI S. Color stability of nanofilled and microhybrid resin-based composites following exposure to chlorhexidine mouthrinses: an in vitro study. J Dent (Tehran) 2016; 13(2): 116-125. https://www.ncbi.nlm.nih.gov/pmc/articles/PMC5139929/
PENUGONDA B, SETTEMBRINI L, SCHERER W, HITTELMAN E, STRASSLER H. Alcohol-containing mouthwashes: effect on composite hardness. J Clin Dent 1994; 5(2): 60-62.
CAVALCANTI AN, MITSUI FHO, AMBROSANO GMB, MATHIAS P, MARCHI GM. Effect of different mouthrinses on Knoop hardness of a restorative composite. Am J Dent 2005; 18(6): 338-340. http://doi.org/10.4172/2161-1122.1000208
YAP AUJ, TAN BWY, TAY LC, CHANG KM, LOY TK, MOK BYY. Effect of mouthrinses on microhardness and wear of composite and compomer restoratives. Oper Dent 2003; 28(6): 740-746.
CHEN L, YU Q, WANG Y, LI H. BisGMA/TEGDMA dental composite containing high aspect-ratio hydroxyapatite nanofibers. Dent Mater 2011; 27(11): 1187-1195. https://doi.org/10.1016/j.dental.2011.08.403
Published
How to Cite
Issue
Section
License
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
La revista Anales del Sistema Sanitario de Navarra es publicada por el Departamento de Salud del Gobierno de Navarra (España), quien conserva los derechos patrimoniales (copyright ) sobre el artículo publicado y favorece y permite la difusión del mismo bajo licencia Creative Commons Reconocimiento-CompartirIgual 4.0 Internacional (CC BY-SA 4.0). Esta licencia permite copiar, usar, difundir, transmitir y exponer públicamente el artículo, siempre que siempre que se cite la autoría y la publicación inicial en Anales del Sistema Sanitario de Navarra, y se distinga la existencia de esta licencia de uso.